The critical analysis of literary hydrogen sorption properties data of Laves phases was carried out in present work. The influence of replacement of Fe by other metals in ZrFe2 on interaction with hydrogen for alloys was experimentally studied. It is established that these intermetallics absorb 1. 6 - 1. 8 wt. % H2 at room temperature. The analysis of correlation of hydrogen capacity and thermodynamic functions from composition of pseudobinary IMC was investigated. These ZrFe2-based alloys are perspective materials for metal-hydrogen compressors which can produce 300 – 800 atm pressure in storage and hydrogen transportation systems.
lingua: Inglese
Conoscenza delle lingue: Madrelingua, Competenza, Avanzate
Login o registrati per correggere questo testo!
Puoi correggere questo testo se specifichi inglese su uno dei seguenti livelli: Madrelingua, Competenza, Avanzate
Puoi correggere questo testo se specifichi inglese su uno dei seguenti livelli: Madrelingua, Competenza, Avanzate
Si prega di correggere i testi su inglese:
Si prega di aiutare con la traduzione:
Arabo Armeno Azero Basco Bielorusso Bosniaco Bulgaro Catalano Ceco Cinese Coreano Croato Danese Ebraico Esperanto Estone Finlandese Francese Gallese Georgiano Giapponese Giavanese Greco Gujarati Hindi Indonesiano Inglese Islandese Italiano Kazako Kyrgyzstani Latino Lettone Macedone Malese Mongolo Norvegese Norwegian (Nynorsk) Olandese Persiano Polacco Portoghese Rumeno Russo Sanscrito Serbo-Croatian Slovacco Spagnolo Svedese Tatarico Tedesco Thai Turco Ucraino Ungherese Uzbeko Vietnamito